ASTM A369 Grade FP11 vs. S31803 Stainless Steel

Both ASTM A369 grade FP11 and S31803 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP11 and the bottom bar is S31803 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
29
Fatigue Strength, MPa 160
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 300
460
Tensile Strength: Ultimate (UTS), MPa 470
710
Tensile Strength: Yield (Proof), MPa 240
500

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 430
1060
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
3.6
Embodied Energy, MJ/kg 21
49
Embodied Water, L/kg 52
160

Common Calculations

PREN (Pitting Resistance) 3.0
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
180
Resilience: Unit (Modulus of Resilience), kJ/m3 150
630
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
25
Strength to Weight: Bending, points 17
23
Thermal Diffusivity, mm2/s 11
4.3
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.030
Chromium (Cr), % 1.0 to 1.5
21 to 23
Iron (Fe), % 96.1 to 97.7
63.7 to 71.9
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.44 to 0.65
2.5 to 3.5
Nickel (Ni), % 0
4.5 to 6.5
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.5 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.020