ASTM A369 Grade FP11 vs. S33425 Stainless Steel

Both ASTM A369 grade FP11 and S33425 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 55% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP11 and the bottom bar is S33425 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
45
Fatigue Strength, MPa 160
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 300
400
Tensile Strength: Ultimate (UTS), MPa 470
580
Tensile Strength: Yield (Proof), MPa 240
230

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
27
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
5.1
Embodied Energy, MJ/kg 21
71
Embodied Water, L/kg 52
190

Common Calculations

PREN (Pitting Resistance) 3.0
30
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
210
Resilience: Unit (Modulus of Resilience), kJ/m3 150
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 11
3.7
Thermal Shock Resistance, points 14
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0.050 to 0.15
0 to 0.080
Chromium (Cr), % 1.0 to 1.5
21 to 23
Iron (Fe), % 96.1 to 97.7
47.2 to 56.7
Manganese (Mn), % 0.3 to 0.6
0 to 1.5
Molybdenum (Mo), % 0.44 to 0.65
2.0 to 3.0
Nickel (Ni), % 0
20 to 23
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.5 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0.15 to 0.6