ASTM A369 Grade FP12 vs. ASTM A372 Grade M Steel
Both ASTM A369 grade FP12 and ASTM A372 grade M steel are iron alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is ASTM A369 grade FP12 and the bottom bar is ASTM A372 grade M steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 240 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 | |
| 18 to 21 |
| Fatigue Strength, MPa | 170 | |
| 450 to 520 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 300 | |
| 510 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 810 to 910 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 660 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 450 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 46 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 9.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 5.0 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.0 |
| Embodied Energy, MJ/kg | 21 | |
| 27 |
| Embodied Water, L/kg | 52 | |
| 61 |
Common Calculations
| PREN (Pitting Resistance) | 2.8 | |
| 3.4 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 | |
| 1140 to 1580 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 29 to 32 |
| Strength to Weight: Bending, points | 17 | |
| 24 to 27 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 14 | |
| 24 to 27 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.23 |
| Chromium (Cr), % | 0.8 to 1.3 | |
| 1.5 to 2.0 |
| Iron (Fe), % | 96.8 to 98.4 | |
| 92.5 to 95.1 |
| Manganese (Mn), % | 0.3 to 0.61 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0.4 to 0.6 |
| Nickel (Ni), % | 0 | |
| 2.8 to 3.9 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Vanadium (V), % | 0 | |
| 0 to 0.080 |