ASTM A369 Grade FP2 vs. ASTM A387 Grade 5 Steel
Both ASTM A369 grade FP2 and ASTM A387 grade 5 steel are iron alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is ASTM A369 grade FP2 and the bottom bar is ASTM A387 grade 5 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 | |
| 150 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 | |
| 20 to 21 |
| Fatigue Strength, MPa | 160 | |
| 160 to 240 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 74 |
| Shear Strength, MPa | 270 | |
| 310 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 500 to 600 |
| Tensile Strength: Yield (Proof), MPa | 240 | |
| 230 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 510 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 49 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 9.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 4.3 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.7 |
| Embodied Energy, MJ/kg | 20 | |
| 23 |
| Embodied Water, L/kg | 50 | |
| 69 |
Common Calculations
| PREN (Pitting Resistance) | 2.5 | |
| 6.8 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 75 | |
| 83 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 | |
| 140 to 320 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 16 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 13 | |
| 11 |
| Thermal Shock Resistance, points | 13 | |
| 14 to 17 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0.5 to 0.81 | |
| 4.0 to 6.0 |
| Iron (Fe), % | 97.4 to 98.6 | |
| 92.1 to 95.3 |
| Manganese (Mn), % | 0.3 to 0.61 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0.45 to 0.65 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.1 to 0.3 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |