ASTM A369 Grade FP22 vs. EN 1.6580 Steel

Both ASTM A369 grade FP22 and EN 1.6580 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is ASTM A369 grade FP22 and the bottom bar is EN 1.6580 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
220 to 350
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
11 to 19
Fatigue Strength, MPa 160
310 to 610
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 300
450 to 700
Tensile Strength: Ultimate (UTS), MPa 470
720 to 1170
Tensile Strength: Yield (Proof), MPa 240
460 to 990

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
450
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
4.3
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.7
1.8
Embodied Energy, MJ/kg 23
23
Embodied Water, L/kg 58
59

Common Calculations

PREN (Pitting Resistance) 5.5
3.3
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 150
560 to 2590
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
26 to 41
Strength to Weight: Bending, points 17
23 to 31
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 14
21 to 34

Alloy Composition

Carbon (C), % 0.050 to 0.15
0.26 to 0.34
Chromium (Cr), % 1.9 to 2.6
1.8 to 2.2
Iron (Fe), % 95 to 96.9
93.7 to 95.5
Manganese (Mn), % 0.3 to 0.6
0.3 to 0.6
Molybdenum (Mo), % 0.87 to 1.1
0.3 to 0.5
Nickel (Ni), % 0
1.8 to 2.2
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.035