ASTM A369 Grade FP9 vs. EN 1.4439 Stainless Steel

Both ASTM A369 grade FP9 and EN 1.4439 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP9 and the bottom bar is EN 1.4439 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
40
Fatigue Strength, MPa 160
270
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
79
Shear Strength, MPa 300
470
Tensile Strength: Ultimate (UTS), MPa 470
680
Tensile Strength: Yield (Proof), MPa 240
310

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Mechanical, °C 600
980
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 26
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 10
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.0
4.5
Embodied Energy, MJ/kg 28
61
Embodied Water, L/kg 87
160

Common Calculations

PREN (Pitting Resistance) 12
35
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
220
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 6.9
3.8
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 8.0 to 10
16.5 to 18.5
Iron (Fe), % 87.1 to 90.3
58.7 to 66.9
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.1
4.0 to 5.0
Nickel (Ni), % 0
12.5 to 14.5
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.5 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015