ASTM A369 Grade FP9 vs. S33228 Stainless Steel

Both ASTM A369 grade FP9 and S33228 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 49% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP9 and the bottom bar is S33228 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
34
Fatigue Strength, MPa 160
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
79
Shear Strength, MPa 300
380
Tensile Strength: Ultimate (UTS), MPa 470
570
Tensile Strength: Yield (Proof), MPa 240
210

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Mechanical, °C 600
1100
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
37
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.0
6.2
Embodied Energy, MJ/kg 28
89
Embodied Water, L/kg 87
220

Common Calculations

PREN (Pitting Resistance) 12
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
150
Resilience: Unit (Modulus of Resilience), kJ/m3 140
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Shock Resistance, points 13
13

Alloy Composition

Aluminum (Al), % 0
0 to 0.025
Carbon (C), % 0 to 0.15
0.040 to 0.080
Cerium (Ce), % 0
0.050 to 0.1
Chromium (Cr), % 8.0 to 10
26 to 28
Iron (Fe), % 87.1 to 90.3
36.5 to 42.3
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
31 to 33
Niobium (Nb), % 0
0.6 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0.5 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.015