ASTM A369 Grade FP91 vs. EN 1.0580 Steel

Both ASTM A369 grade FP91 and EN 1.0580 steel are iron alloys. They have 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP91 and the bottom bar is EN 1.0580 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
5.6 to 25
Fatigue Strength, MPa 320
210 to 270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Shear Strength, MPa 410
340 to 360
Tensile Strength: Ultimate (UTS), MPa 670
540 to 620
Tensile Strength: Yield (Proof), MPa 460
290 to 450

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 600
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 37
18
Embodied Water, L/kg 88
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
31 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 560
230 to 540
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
19 to 22
Strength to Weight: Bending, points 22
19 to 21
Thermal Diffusivity, mm2/s 6.9
14
Thermal Shock Resistance, points 18
17 to 20

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Carbon (C), % 0.080 to 0.12
0 to 0.22
Chromium (Cr), % 8.0 to 9.5
0
Iron (Fe), % 87.3 to 90.3
97.5 to 100
Manganese (Mn), % 0.3 to 0.6
0 to 1.6
Molybdenum (Mo), % 0.85 to 1.1
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.060 to 0.1
0
Nitrogen (N), % 0.030 to 0.070
0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.2 to 0.5
0 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.045
Titanium (Ti), % 0 to 0.010
0
Vanadium (V), % 0.18 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0