ASTM A369 Grade FP91 vs. EN 2.4608 Nickel
ASTM A369 grade FP91 belongs to the iron alloys classification, while EN 2.4608 nickel belongs to the nickel alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A369 grade FP91 and the bottom bar is EN 2.4608 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 19 | |
| 34 |
| Fatigue Strength, MPa | 320 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 81 |
| Shear Strength, MPa | 410 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 670 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Conductivity, W/m-K | 26 | |
| 11 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.9 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 55 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 8.4 |
| Embodied Energy, MJ/kg | 37 | |
| 120 |
| Embodied Water, L/kg | 88 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 | |
| 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 24 | |
| 20 |
| Strength to Weight: Bending, points | 22 | |
| 19 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 2.9 |
| Thermal Shock Resistance, points | 18 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.020 | |
| 0 |
| Carbon (C), % | 0.080 to 0.12 | |
| 0.030 to 0.080 |
| Chromium (Cr), % | 8.0 to 9.5 | |
| 24 to 26 |
| Cobalt (Co), % | 0 | |
| 2.5 to 4.0 |
| Iron (Fe), % | 87.3 to 90.3 | |
| 11.4 to 23.8 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.85 to 1.1 | |
| 2.5 to 4.0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 44 to 47 |
| Niobium (Nb), % | 0.060 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0.030 to 0.070 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.5 | |
| 0.7 to 1.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 | |
| 2.5 to 4.0 |
| Vanadium (V), % | 0.18 to 0.25 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.010 | |
| 0 |