ASTM A372 Grade J Steel vs. SAE-AISI M36 Steel
Both ASTM A372 grade J steel and SAE-AISI M36 steel are iron alloys. They have 75% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is SAE-AISI M36 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 1020 | |
| 810 to 2190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1600 |
| Melting Onset (Solidus), °C | 1420 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Conductivity, W/m-K | 44 | |
| 19 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 38 |
| Density, g/cm3 | 7.8 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 9.5 |
| Embodied Energy, MJ/kg | 20 | |
| 140 |
| Embodied Water, L/kg | 51 | |
| 140 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 23 to 36 | |
| 27 to 72 |
| Strength to Weight: Bending, points | 21 to 29 | |
| 23 to 44 |
| Thermal Diffusivity, mm2/s | 12 | |
| 5.1 |
| Thermal Shock Resistance, points | 19 to 30 | |
| 25 to 68 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.5 | |
| 0.8 to 0.9 |
| Chromium (Cr), % | 0.8 to 1.2 | |
| 3.8 to 4.5 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 96.7 to 97.8 | |
| 70.1 to 75.5 |
| Manganese (Mn), % | 0.75 to 1.1 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 4.6 to 5.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0.2 to 0.45 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 5.5 to 6.5 |
| Vanadium (V), % | 0 | |
| 1.8 to 2.3 |