ASTM A372 Grade L Steel vs. EN 1.0511 Steel
Both ASTM A372 grade L steel and EN 1.0511 steel are iron alloys. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is ASTM A372 grade L steel and the bottom bar is EN 1.0511 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 350 | |
| 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 | |
| 17 |
| Fatigue Strength, MPa | 670 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 700 | |
| 370 |
| Tensile Strength: Ultimate (UTS), MPa | 1160 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 1040 | |
| 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 44 | |
| 48 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.5 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 22 | |
| 19 |
| Embodied Water, L/kg | 54 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2890 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 41 | |
| 21 |
| Strength to Weight: Bending, points | 31 | |
| 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 13 |
| Thermal Shock Resistance, points | 34 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.38 to 0.43 | |
| 0.37 to 0.44 |
| Chromium (Cr), % | 0.7 to 0.9 | |
| 0 to 0.4 |
| Iron (Fe), % | 95.2 to 96.3 | |
| 97.4 to 99.13 |
| Manganese (Mn), % | 0.6 to 0.8 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 0 to 0.1 |
| Nickel (Ni), % | 1.7 to 2.0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.045 |