ASTM A372 Grade M Steel vs. ACI-ASTM CB7Cu-1 Steel
Both ASTM A372 grade M steel and ACI-ASTM CB7Cu-1 steel are iron alloys. They have 81% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A372 grade M steel and the bottom bar is ACI-ASTM CB7Cu-1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 to 280 | |
| 300 to 420 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 21 | |
| 5.7 to 11 |
| Fatigue Strength, MPa | 450 to 520 | |
| 420 to 590 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 910 | |
| 960 to 1350 |
| Tensile Strength: Yield (Proof), MPa | 660 to 770 | |
| 760 to 1180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 46 | |
| 17 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 2.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 13 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 27 | |
| 38 |
| Embodied Water, L/kg | 61 | |
| 130 |
Common Calculations
| PREN (Pitting Resistance) | 3.4 | |
| 17 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 71 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1140 to 1580 | |
| 1500 to 3590 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 29 to 32 | |
| 34 to 48 |
| Strength to Weight: Bending, points | 24 to 27 | |
| 28 to 35 |
| Thermal Diffusivity, mm2/s | 12 | |
| 4.6 |
| Thermal Shock Resistance, points | 24 to 27 | |
| 32 to 45 |
Alloy Composition
| Carbon (C), % | 0 to 0.23 | |
| 0 to 0.070 |
| Chromium (Cr), % | 1.5 to 2.0 | |
| 15.5 to 17.7 |
| Copper (Cu), % | 0 | |
| 2.5 to 3.2 |
| Iron (Fe), % | 92.5 to 95.1 | |
| 72.3 to 78.4 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 to 0.7 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0 |
| Nickel (Ni), % | 2.8 to 3.9 | |
| 3.6 to 4.6 |
| Niobium (Nb), % | 0 | |
| 0 to 0.35 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.080 | |
| 0 |