ASTM A372 Grade M Steel vs. EN 1.7711 Steel
Both ASTM A372 grade M steel and EN 1.7711 steel are iron alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is ASTM A372 grade M steel and the bottom bar is EN 1.7711 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 to 280 | |
| 210 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 21 | |
| 16 to 22 |
| Fatigue Strength, MPa | 450 to 520 | |
| 290 to 520 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 510 to 570 | |
| 440 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 910 | |
| 690 to 930 |
| Tensile Strength: Yield (Proof), MPa | 660 to 770 | |
| 400 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 450 | |
| 430 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 33 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 3.0 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 2.3 |
| Embodied Energy, MJ/kg | 27 | |
| 32 |
| Embodied Water, L/kg | 61 | |
| 54 |
Common Calculations
| PREN (Pitting Resistance) | 3.4 | |
| 2.9 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 130 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1140 to 1580 | |
| 430 to 1690 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 29 to 32 | |
| 24 to 33 |
| Strength to Weight: Bending, points | 24 to 27 | |
| 22 to 27 |
| Thermal Diffusivity, mm2/s | 12 | |
| 8.9 |
| Thermal Shock Resistance, points | 24 to 27 | |
| 24 to 32 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 to 0.23 | |
| 0.36 to 0.44 |
| Chromium (Cr), % | 1.5 to 2.0 | |
| 0.9 to 1.2 |
| Iron (Fe), % | 92.5 to 95.1 | |
| 96 to 97.5 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0.45 to 0.85 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0.5 to 0.65 |
| Nickel (Ni), % | 2.8 to 3.9 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.080 | |
| 0.25 to 0.35 |