ASTM A372 Grade M Steel vs. C95300 Bronze
ASTM A372 grade M steel belongs to the iron alloys classification, while C95300 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A372 grade M steel and the bottom bar is C95300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 to 280 | |
| 120 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 18 to 21 | |
| 14 to 25 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 910 | |
| 520 to 610 |
| Tensile Strength: Yield (Proof), MPa | 660 to 770 | |
| 190 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 450 | |
| 220 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1050 |
| Melting Onset (Solidus), °C | 1420 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Conductivity, W/m-K | 46 | |
| 63 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 28 |
| Density, g/cm3 | 7.9 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 3.1 |
| Embodied Energy, MJ/kg | 27 | |
| 52 |
| Embodied Water, L/kg | 61 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 73 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1140 to 1580 | |
| 170 to 420 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 29 to 32 | |
| 17 to 21 |
| Strength to Weight: Bending, points | 24 to 27 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 12 | |
| 17 |
| Thermal Shock Resistance, points | 24 to 27 | |
| 19 to 22 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 9.0 to 11 |
| Carbon (C), % | 0 to 0.23 | |
| 0 |
| Chromium (Cr), % | 1.5 to 2.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 86.5 to 90.2 |
| Iron (Fe), % | 92.5 to 95.1 | |
| 0.8 to 1.5 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0 |
| Nickel (Ni), % | 2.8 to 3.9 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Vanadium (V), % | 0 to 0.080 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 1.0 |