ASTM A387 Grade 11 Steel vs. EN 1.4477 Stainless Steel
Both ASTM A387 grade 11 steel and EN 1.4477 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is EN 1.4477 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 180 | |
| 270 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 25 | |
| 22 to 23 |
| Fatigue Strength, MPa | 200 to 250 | |
| 420 to 490 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 73 | |
| 81 |
| Shear Strength, MPa | 320 to 390 | |
| 550 to 580 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 880 to 930 |
| Tensile Strength: Yield (Proof), MPa | 270 to 350 | |
| 620 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 39 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.9 | |
| 20 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 3.7 |
| Embodied Energy, MJ/kg | 21 | |
| 52 |
| Embodied Water, L/kg | 53 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 3.1 | |
| 41 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 130 | |
| 180 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 320 | |
| 940 to 1290 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 31 to 33 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 26 to 27 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.5 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 23 to 25 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.17 | |
| 0 to 0.030 |
| Chromium (Cr), % | 1.0 to 1.5 | |
| 28 to 30 |
| Copper (Cu), % | 0 | |
| 0 to 0.8 |
| Iron (Fe), % | 96.2 to 97.6 | |
| 56.6 to 63.6 |
| Manganese (Mn), % | 0.4 to 0.65 | |
| 0.8 to 1.5 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 1.5 to 2.6 |
| Nickel (Ni), % | 0 | |
| 5.8 to 7.5 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.5 to 0.8 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |