ASTM A387 Grade 11 Steel vs. Titanium 6-6-2
ASTM A387 grade 11 steel belongs to the iron alloys classification, while titanium 6-6-2 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 11 steel and the bottom bar is titanium 6-6-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 25 | |
| 6.7 to 9.0 |
| Fatigue Strength, MPa | 200 to 250 | |
| 590 to 670 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 44 |
| Shear Strength, MPa | 320 to 390 | |
| 670 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 1140 to 1370 |
| Tensile Strength: Yield (Proof), MPa | 270 to 350 | |
| 1040 to 1230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 310 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1610 |
| Melting Onset (Solidus), °C | 1420 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 39 | |
| 5.5 |
| Thermal Expansion, µm/m-K | 13 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 1.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.9 | |
| 40 |
| Density, g/cm3 | 7.8 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 29 |
| Embodied Energy, MJ/kg | 21 | |
| 470 |
| Embodied Water, L/kg | 53 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 130 | |
| 89 to 99 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 34 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 66 to 79 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 11 | |
| 2.1 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 75 to 90 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.0 to 6.0 |
| Carbon (C), % | 0.050 to 0.17 | |
| 0 to 0.050 |
| Chromium (Cr), % | 1.0 to 1.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.35 to 1.0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 96.2 to 97.6 | |
| 0.35 to 1.0 |
| Manganese (Mn), % | 0.4 to 0.65 | |
| 0 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 5.0 to 6.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.5 to 0.8 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 82.8 to 87.8 |
| Residuals, % | 0 | |
| 0 to 0.4 |