ASTM A387 Grade 2 Steel vs. EN 1.4313 Stainless Steel
Both ASTM A387 grade 2 steel and EN 1.4313 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 2 steel and the bottom bar is EN 1.4313 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 25 | |
| 12 to 17 |
| Fatigue Strength, MPa | 190 to 250 | |
| 340 to 510 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 300 to 350 | |
| 460 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 550 | |
| 750 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 260 to 350 | |
| 580 to 910 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 780 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 45 | |
| 25 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 10 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.4 |
| Embodied Energy, MJ/kg | 20 | |
| 34 |
| Embodied Water, L/kg | 50 | |
| 110 |
Common Calculations
| PREN (Pitting Resistance) | 2.4 | |
| 15 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 120 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 320 | |
| 870 to 2100 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 27 to 36 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 23 to 28 |
| Thermal Diffusivity, mm2/s | 12 | |
| 6.7 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 27 to 36 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.21 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 12 to 14 |
| Iron (Fe), % | 97.1 to 98.3 | |
| 78.5 to 84.2 |
| Manganese (Mn), % | 0.55 to 0.8 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.45 to 0.6 | |
| 0.3 to 0.7 |
| Nickel (Ni), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |