ASTM A387 Grade 21 Steel vs. EN 1.8870 Steel
Both ASTM A387 grade 21 steel and EN 1.8870 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 21 steel and the bottom bar is EN 1.8870 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 180 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 21 | |
| 21 |
| Fatigue Strength, MPa | 160 to 250 | |
| 310 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Shear Strength, MPa | 310 to 370 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 590 | |
| 610 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 480 | |
| 410 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 | |
| 39 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.1 | |
| 2.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 1.7 |
| Embodied Energy, MJ/kg | 23 | |
| 22 |
| Embodied Water, L/kg | 62 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 to 110 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 320 | |
| 530 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 22 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 10 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 18 |
Alloy Composition
| Boron (B), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.18 |
| Chromium (Cr), % | 2.8 to 3.3 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 94.4 to 96 | |
| 95.1 to 100 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 1.7 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Niobium (Nb), % | 0 | |
| 0 to 0.050 |
| Nitrogen (N), % | 0 | |
| 0 to 0.015 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0 to 0.080 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |