ASTM A387 Grade 21 Steel vs. Monel R-405
ASTM A387 grade 21 steel belongs to the iron alloys classification, while Monel R-405 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 21 steel and the bottom bar is Monel R-405.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 160 |
| Elongation at Break, % | 21 | |
| 9.1 to 39 |
| Fatigue Strength, MPa | 160 to 250 | |
| 210 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 74 | |
| 62 |
| Shear Strength, MPa | 310 to 370 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 590 | |
| 540 to 630 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 190 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 480 | |
| 900 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1350 |
| Melting Onset (Solidus), °C | 1430 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 41 | |
| 23 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.1 | |
| 50 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 7.9 |
| Embodied Energy, MJ/kg | 23 | |
| 110 |
| Embodied Water, L/kg | 62 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 to 110 | |
| 49 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 320 | |
| 120 to 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 10 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 17 to 20 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 11 | |
| 5.9 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 17 to 20 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.3 |
| Chromium (Cr), % | 2.8 to 3.3 | |
| 0 |
| Copper (Cu), % | 0 | |
| 28 to 34 |
| Iron (Fe), % | 94.4 to 96 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 63 to 72 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.025 to 0.060 |