ASTM A387 Grade 21L Class 1 vs. EN 1.8866 Steel

Both ASTM A387 grade 21L class 1 and EN 1.8866 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 21L class 1 and the bottom bar is EN 1.8866 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
25
Fatigue Strength, MPa 160
260
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 310
350
Tensile Strength: Ultimate (UTS), MPa 500
540
Tensile Strength: Yield (Proof), MPa 230
350

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 480
410
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
48
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.8
1.6
Embodied Energy, MJ/kg 23
21
Embodied Water, L/kg 62
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
330
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 14
16

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.1
0 to 0.16
Chromium (Cr), % 2.8 to 3.3
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 94.4 to 96.1
96.3 to 100
Manganese (Mn), % 0.3 to 0.6
0 to 1.5
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.25
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.060
Zirconium (Zr), % 0
0 to 0.050