ASTM A387 Grade 21L Class 1 vs. Type 2 Niobium
ASTM A387 grade 21L class 1 belongs to the iron alloys classification, while Type 2 niobium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 21L class 1 and the bottom bar is Type 2 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 150 | |
110 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
110 |
Elongation at Break, % | 21 | |
29 |
Poisson's Ratio | 0.29 | |
0.4 |
Shear Modulus, GPa | 74 | |
38 |
Tensile Strength: Ultimate (UTS), MPa | 500 | |
140 |
Tensile Strength: Yield (Proof), MPa | 230 | |
82 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
320 |
Specific Heat Capacity, J/kg-K | 470 | |
270 |
Thermal Conductivity, W/m-K | 41 | |
52 |
Thermal Expansion, µm/m-K | 13 | |
7.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.9 | |
8.6 |
Embodied Water, L/kg | 62 | |
160 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 | |
35 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
32 |
Stiffness to Weight: Axial, points | 13 | |
6.8 |
Stiffness to Weight: Bending, points | 24 | |
18 |
Strength to Weight: Axial, points | 18 | |
4.6 |
Strength to Weight: Bending, points | 18 | |
7.1 |
Thermal Diffusivity, mm2/s | 11 | |
23 |
Thermal Shock Resistance, points | 14 | |
13 |
Alloy Composition
Carbon (C), % | 0 to 0.1 | |
0 to 0.010 |
Chromium (Cr), % | 2.8 to 3.3 | |
0 |
Hafnium (Hf), % | 0 | |
0 to 0.020 |
Hydrogen (H), % | 0 | |
0 to 0.0015 |
Iron (Fe), % | 94.4 to 96.1 | |
0 to 0.010 |
Manganese (Mn), % | 0.3 to 0.6 | |
0 |
Molybdenum (Mo), % | 0.9 to 1.1 | |
0 to 0.020 |
Nickel (Ni), % | 0 | |
0 to 0.0050 |
Niobium (Nb), % | 0 | |
99.5 to 100 |
Nitrogen (N), % | 0 | |
0 to 0.010 |
Oxygen (O), % | 0 | |
0 to 0.025 |
Phosphorus (P), % | 0 to 0.025 | |
0 |
Silicon (Si), % | 0 to 0.5 | |
0 to 0.0050 |
Sulfur (S), % | 0 to 0.025 | |
0 |
Tantalum (Ta), % | 0 | |
0 to 0.3 |
Titanium (Ti), % | 0 | |
0 to 0.030 |
Tungsten (W), % | 0 | |
0 to 0.050 |
Zirconium (Zr), % | 0 | |
0 to 0.020 |