ASTM A387 Grade 22 Steel vs. ASTM A356 Grade 1

Both ASTM A387 grade 22 steel and ASTM A356 grade 1 are iron alloys. They have a very high 97% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 22 steel and the bottom bar is ASTM A356 grade 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
23
Fatigue Strength, MPa 160 to 240
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 480 to 600
550
Tensile Strength: Yield (Proof), MPa 230 to 350
280

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 58
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 85 to 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 320
210
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17 to 21
20
Strength to Weight: Bending, points 17 to 20
19
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 14 to 17
18

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.35
Chromium (Cr), % 2.0 to 2.5
0
Iron (Fe), % 95.1 to 96.8
98.3 to 100
Manganese (Mn), % 0.3 to 0.6
0 to 0.7
Molybdenum (Mo), % 0.9 to 1.1
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030