ASTM A387 Grade 5 Steel vs. AWS ER70S-A1
Both ASTM A387 grade 5 steel and AWS ER70S-A1 are iron alloys. They have a very high 95% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM A387 grade 5 steel and the bottom bar is AWS ER70S-A1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 to 21 | |
| 22 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 40 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.3 | |
| 2.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 23 | |
| 20 |
| Embodied Water, L/kg | 69 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 110 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 320 | |
| 540 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 21 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 14 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.12 |
| Chromium (Cr), % | 4.0 to 6.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.35 |
| Iron (Fe), % | 92.1 to 95.3 | |
| 96.1 to 99.3 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 1.3 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 0.4 to 0.65 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.3 to 0.7 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |
| Residuals, % | 0 | |
| 0 to 0.5 |