ASTM A387 Grade 5 Steel vs. EN 1.7233 Steel
Both ASTM A387 grade 5 steel and EN 1.7233 steel are iron alloys. They have a very high 96% of their average alloy composition in common.
For each property being compared, the top bar is ASTM A387 grade 5 steel and the bottom bar is EN 1.7233 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 180 | |
| 210 to 290 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 to 21 | |
| 18 to 23 |
| Fatigue Strength, MPa | 160 to 240 | |
| 270 to 530 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Shear Strength, MPa | 310 to 380 | |
| 450 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 600 | |
| 700 to 960 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 380 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 510 | |
| 430 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 40 | |
| 39 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.3 | |
| 3.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.6 |
| Embodied Energy, MJ/kg | 23 | |
| 21 |
| Embodied Water, L/kg | 69 | |
| 53 |
Common Calculations
| PREN (Pitting Resistance) | 6.8 | |
| 3.3 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 110 | |
| 110 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 320 | |
| 380 to 1630 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 25 to 34 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 22 to 28 |
| Thermal Diffusivity, mm2/s | 11 | |
| 11 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 21 to 28 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0.39 to 0.45 |
| Chromium (Cr), % | 4.0 to 6.0 | |
| 1.2 to 1.5 |
| Iron (Fe), % | 92.1 to 95.3 | |
| 96.2 to 97.5 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 0.5 to 0.7 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.035 |