ASTM A387 Grade 5 Steel vs. SAE-AISI 6118 Steel

Both ASTM A387 grade 5 steel and SAE-AISI 6118 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A387 grade 5 steel and the bottom bar is SAE-AISI 6118 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20 to 21
23
Fatigue Strength, MPa 160 to 240
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 310 to 380
300
Tensile Strength: Ultimate (UTS), MPa 500 to 600
470
Tensile Strength: Yield (Proof), MPa 230 to 350
290

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
45
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.7
Embodied Energy, MJ/kg 23
23
Embodied Water, L/kg 69
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 110
93
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 320
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18 to 21
17
Strength to Weight: Bending, points 18 to 20
17
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 14 to 17
14

Alloy Composition

Carbon (C), % 0 to 0.15
0.16 to 0.21
Chromium (Cr), % 4.0 to 6.0
0.5 to 0.7
Iron (Fe), % 92.1 to 95.3
97.8 to 98.6
Manganese (Mn), % 0.3 to 0.6
0.5 to 0.7
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.040
Vanadium (V), % 0
0.1 to 0.15