ASTM A514 Steel vs. Solder Alloy 704
ASTM A514 steel belongs to the iron alloys classification, while solder alloy 704 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ASTM A514 steel and the bottom bar is solder alloy 704.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 to 250 | |
| 14 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 51 |
| Elongation at Break, % | 18 to 21 | |
| 30 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 73 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 830 | |
| 55 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 260 | |
| 62 |
| Melting Completion (Liquidus), °C | 1460 | |
| 240 |
| Melting Onset (Solidus), °C | 1420 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 220 |
| Thermal Conductivity, W/m-K | 37 to 51 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.6 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 to 8.8 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 1.6 to 1.8 | |
| 19 |
| Embodied Energy, MJ/kg | 21 to 25 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 17 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 2.1 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 4.3 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 30 |
| Thermal Shock Resistance, points | 23 to 24 | |
| 3.5 |