ASTM A514 Steel vs. C61000 Bronze
ASTM A514 steel belongs to the iron alloys classification, while C61000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A514 steel and the bottom bar is C61000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 18 to 21 | |
| 29 to 50 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 42 |
| Shear Strength, MPa | 490 to 520 | |
| 280 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 830 | |
| 390 to 460 |
| Tensile Strength: Yield (Proof), MPa | 690 to 770 | |
| 150 to 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 260 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 400 to 440 | |
| 210 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1040 |
| Melting Onset (Solidus), °C | 1420 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 420 |
| Thermal Conductivity, W/m-K | 37 to 51 | |
| 69 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.6 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 to 8.8 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 to 3.8 | |
| 29 |
| Density, g/cm3 | 7.8 to 7.9 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.6 to 1.8 | |
| 3.0 |
| Embodied Energy, MJ/kg | 21 to 25 | |
| 49 |
| Embodied Water, L/kg | 48 to 57 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 170 | |
| 110 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1280 to 1590 | |
| 100 to 160 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 13 to 15 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 14 to 16 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 19 |
| Thermal Shock Resistance, points | 23 to 24 | |
| 14 to 16 |