ASTM A572 Steel vs. EN 1.4542 Stainless Steel
Both ASTM A572 steel and EN 1.4542 stainless steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A572 steel and the bottom bar is EN 1.4542 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 25 | |
| 5.7 to 20 |
| Fatigue Strength, MPa | 240 to 340 | |
| 370 to 640 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 300 to 380 | |
| 550 to 860 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 620 | |
| 880 to 1470 |
| Tensile Strength: Yield (Proof), MPa | 330 to 510 | |
| 580 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 860 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.3 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 13 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 22 | |
| 39 |
| Embodied Water, L/kg | 47 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 110 | |
| 62 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 690 | |
| 880 to 4360 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 22 | |
| 31 to 52 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 26 to 37 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.3 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 29 to 49 |