MakeItFrom.com
Menu (ESC)

ASTM A572 Steel vs. CC755S Brass

ASTM A572 steel belongs to the iron alloys classification, while CC755S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A572 steel and the bottom bar is CC755S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 190
110
Elastic (Young's, Tensile) Modulus, GPa 190
100
Elongation at Break, % 18 to 25
9.5
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 73
40
Tensile Strength: Ultimate (UTS), MPa 470 to 620
390
Tensile Strength: Yield (Proof), MPa 330 to 510
250

Thermal Properties

Latent Heat of Fusion, J/g 250
170
Maximum Temperature: Mechanical, °C 400
120
Melting Completion (Liquidus), °C 1460
820
Melting Onset (Solidus), °C 1420
780
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 51
120
Thermal Expansion, µm/m-K 13
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2 to 8.3
30

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
23
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.6
2.7
Embodied Energy, MJ/kg 22
46
Embodied Water, L/kg 47
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100 to 110
33
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 690
290
Stiffness to Weight: Axial, points 13
7.1
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 17 to 22
14
Strength to Weight: Bending, points 17 to 21
15
Thermal Diffusivity, mm2/s 14
38
Thermal Shock Resistance, points 14 to 18
13