ASTM A572 Steel vs. Monel R-405
ASTM A572 steel belongs to the iron alloys classification, while Monel R-405 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A572 steel and the bottom bar is Monel R-405.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 160 |
| Elongation at Break, % | 18 to 25 | |
| 9.1 to 39 |
| Fatigue Strength, MPa | 240 to 340 | |
| 210 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 62 |
| Shear Strength, MPa | 300 to 380 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 620 | |
| 540 to 630 |
| Tensile Strength: Yield (Proof), MPa | 330 to 510 | |
| 190 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 900 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1350 |
| Melting Onset (Solidus), °C | 1420 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 51 | |
| 23 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.3 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 50 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 7.9 |
| Embodied Energy, MJ/kg | 22 | |
| 110 |
| Embodied Water, L/kg | 47 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 110 | |
| 49 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 690 | |
| 120 to 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 10 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 17 to 22 | |
| 17 to 20 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 5.9 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 17 to 20 |