ASTM A572 Steel vs. C70600 Copper-nickel
ASTM A572 steel belongs to the iron alloys classification, while C70600 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A572 steel and the bottom bar is C70600 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 18 to 25 | |
| 3.0 to 34 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 46 |
| Shear Strength, MPa | 300 to 380 | |
| 190 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 620 | |
| 290 to 570 |
| Tensile Strength: Yield (Proof), MPa | 330 to 510 | |
| 63 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 220 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1150 |
| Melting Onset (Solidus), °C | 1420 | |
| 1100 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 51 | |
| 44 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 9.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.3 | |
| 9.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 | |
| 33 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 3.4 |
| Embodied Energy, MJ/kg | 22 | |
| 51 |
| Embodied Water, L/kg | 47 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 110 | |
| 6.5 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 690 | |
| 16 to 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 17 to 22 | |
| 9.1 to 18 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 11 to 17 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 9.8 to 19 |