ASTM A732 Cast Steel vs. ASTM A182 Grade F911

Both ASTM A732 cast steel and ASTM A182 grade F911 are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A732 cast steel and the bottom bar is ASTM A182 grade F911.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 440
220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.0 to 25
20
Fatigue Strength, MPa 230 to 750
350
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72 to 73
76
Tensile Strength: Ultimate (UTS), MPa 460 to 1470
690
Tensile Strength: Yield (Proof), MPa 310 to 1340
500

Thermal Properties

Latent Heat of Fusion, J/g 250 to 260
270
Maximum Temperature: Mechanical, °C 400 to 430
600
Melting Completion (Liquidus), °C 1440 to 1460
1480
Melting Onset (Solidus), °C 1400 to 1420
1440
Specific Heat Capacity, J/kg-K 470 to 480
470
Thermal Conductivity, W/m-K 39 to 50
26
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1 to 7.7
9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2 to 8.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0 to 3.8
9.5
Density, g/cm3 7.8 to 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4 to 1.7
2.8
Embodied Energy, MJ/kg 19 to 24
40
Embodied Water, L/kg 47 to 54
90

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 45 to 130
130
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 4770
650
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 52
24
Strength to Weight: Bending, points 17 to 37
22
Thermal Diffusivity, mm2/s 10 to 14
6.9
Thermal Shock Resistance, points 14 to 43
19