ASTM A732 Cast Steel vs. ASTM A217 Cast Steel
Both ASTM A732 cast steel and ASTM A217 cast steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A732 cast steel and the bottom bar is ASTM A217 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 440 | |
| 160 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 4.0 to 25 | |
| 21 to 27 |
| Fatigue Strength, MPa | 230 to 750 | |
| 200 to 320 |
| Poisson's Ratio | 0.29 | |
| 0.28 to 0.29 |
| Shear Modulus, GPa | 72 to 73 | |
| 73 to 75 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1470 | |
| 540 to 710 |
| Tensile Strength: Yield (Proof), MPa | 310 to 1340 | |
| 270 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 260 | |
| 250 to 270 |
| Maximum Temperature: Mechanical, °C | 400 to 430 | |
| 410 to 600 |
| Melting Completion (Liquidus), °C | 1440 to 1460 | |
| 1450 to 1460 |
| Melting Onset (Solidus), °C | 1400 to 1420 | |
| 1410 to 1420 |
| Specific Heat Capacity, J/kg-K | 470 to 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 to 50 | |
| 26 to 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 to 7.7 | |
| 7.3 to 9.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.9 | |
| 8.4 to 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.0 to 3.8 | |
| 2.4 to 7.0 |
| Density, g/cm3 | 7.8 to 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 to 1.7 | |
| 1.5 to 2.1 |
| Embodied Energy, MJ/kg | 19 to 24 | |
| 20 to 28 |
| Embodied Water, L/kg | 47 to 54 | |
| 47 to 87 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 to 130 | |
| 110 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 4770 | |
| 190 to 570 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 to 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 16 to 52 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 19 to 23 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 6.9 to 14 |
| Thermal Shock Resistance, points | 14 to 43 | |
| 16 to 20 |