ASTM A732 Cast Steel vs. K93600 Alloy
Both ASTM A732 cast steel and K93600 alloy are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ASTM A732 cast steel and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 4.0 to 25 | |
| 5.0 to 35 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1470 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 310 to 1340 | |
| 280 to 750 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 400 to 430 | |
| 440 |
| Melting Onset (Solidus), °C | 1400 to 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 to 480 | |
| 520 |
| Thermal Conductivity, W/m-K | 39 to 50 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 to 7.7 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.9 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 to 130 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 4770 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 16 to 52 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 3.1 |
| Thermal Shock Resistance, points | 14 to 43 | |
| 34 to 57 |