ASTM A732 Cast Steel vs. R05400 Tantalum
ASTM A732 cast steel belongs to the iron alloys classification, while R05400 tantalum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM A732 cast steel and the bottom bar is R05400 tantalum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 4.0 to 25 | |
| 1.1 to 28 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 to 73 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1470 | |
| 210 to 540 |
| Tensile Strength: Yield (Proof), MPa | 310 to 1340 | |
| 140 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 260 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 470 to 480 | |
| 140 |
| Thermal Conductivity, W/m-K | 39 to 50 | |
| 59 |
| Thermal Expansion, µm/m-K | 13 | |
| 6.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 17 |
| Embodied Water, L/kg | 47 to 54 | |
| 650 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 45 to 130 | |
| 5.5 to 53 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 4770 | |
| 50 to 420 |
| Stiffness to Weight: Axial, points | 13 | |
| 6.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 11 |
| Strength to Weight: Axial, points | 16 to 52 | |
| 3.6 to 9.0 |
| Strength to Weight: Bending, points | 17 to 37 | |
| 4.8 to 8.8 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 25 |
| Thermal Shock Resistance, points | 14 to 43 | |
| 13 to 32 |