ASTM B477 Au-Ni-Ag vs. ASTM A217 Cast Steel
ASTM B477 Au-Ni-Ag belongs to the otherwise unclassified metals classification, while ASTM A217 cast steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B477 Au-Ni-Ag and the bottom bar is ASTM A217 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 190 |
| Elongation at Break, % | 5.5 to 11 | |
| 21 to 27 |
| Poisson's Ratio | 0.41 | |
| 0.28 to 0.29 |
| Shear Modulus, GPa | 34 | |
| 73 to 75 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 550 | |
| 540 to 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 80 | |
| 250 to 270 |
| Melting Completion (Liquidus), °C | 1010 | |
| 1450 to 1460 |
| Melting Onset (Solidus), °C | 930 | |
| 1410 to 1420 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 470 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 7.3 to 9.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.5 | |
| 8.4 to 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 7.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 13 to 14 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 5.0 to 9.0 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 6.0 to 8.8 | |
| 19 to 23 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 16 to 20 |