ASTM B477 Au-Ni-Ag vs. Grade 20 Titanium
ASTM B477 Au-Ni-Ag belongs to the otherwise unclassified metals classification, while grade 20 titanium belongs to the titanium alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B477 Au-Ni-Ag and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 120 |
| Elongation at Break, % | 5.5 to 11 | |
| 5.7 to 17 |
| Poisson's Ratio | 0.41 | |
| 0.32 |
| Shear Modulus, GPa | 34 | |
| 47 |
| Shear Strength, MPa | 190 to 320 | |
| 560 to 740 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 550 | |
| 900 to 1270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 80 | |
| 400 |
| Melting Completion (Liquidus), °C | 1010 | |
| 1660 |
| Melting Onset (Solidus), °C | 930 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 520 |
| Thermal Expansion, µm/m-K | 15 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 5.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 33 |
| Strength to Weight: Axial, points | 5.0 to 9.0 | |
| 50 to 70 |
| Strength to Weight: Bending, points | 6.0 to 8.8 | |
| 41 to 52 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 55 to 77 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 5.5 to 6.5 |
| Gold (Au), % | 74.2 to 75.8 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 2.6 to 3.4 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Silver (Ag), % | 21.4 to 22.6 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 71 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |