ASTM B522 Class I vs. SAE-AISI H21 Steel
ASTM B522 class I belongs to the otherwise unclassified metals classification, while SAE-AISI H21 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is ASTM B522 class I and the bottom bar is SAE-AISI H21 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 96 | |
| 200 |
| Poisson's Ratio | 0.41 | |
| 0.29 |
| Shear Modulus, GPa | 34 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 490 | |
| 720 to 1790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 250 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1630 |
| Melting Onset (Solidus), °C | 1030 | |
| 1580 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 440 |
| Thermal Expansion, µm/m-K | 15 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.5 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 23 |
| Strength to Weight: Axial, points | 4.4 to 7.8 | |
| 23 to 58 |
| Strength to Weight: Bending, points | 5.5 to 8.0 | |
| 21 to 38 |
| Thermal Shock Resistance, points | 13 to 24 | |
| 24 to 59 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.28 to 0.36 |
| Chromium (Cr), % | 0 | |
| 3.0 to 3.8 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Gold (Au), % | 68 to 70 | |
| 0 |
| Iron (Fe), % | 0 | |
| 87.6 to 93.8 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Platinum (Pt), % | 5.0 to 7.0 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.5 |
| Silver (Ag), % | 23.5 to 26.5 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 8.5 to 10 |
| Vanadium (V), % | 0 | |
| 0.3 to 0.6 |
| Residuals, % | 0 to 0.35 | |
| 0 |