ASTM B522 Class I vs. C14510 Copper
ASTM B522 class I belongs to the otherwise unclassified metals classification, while C14510 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM B522 class I and the bottom bar is C14510 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 96 | |
| 120 |
| Elongation at Break, % | 1.1 to 29 | |
| 9.1 to 9.6 |
| Poisson's Ratio | 0.41 | |
| 0.34 |
| Shear Modulus, GPa | 34 | |
| 43 |
| Shear Strength, MPa | 180 to 280 | |
| 180 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 490 | |
| 300 to 320 |
| Tensile Strength: Yield (Proof), MPa | 120 to 210 | |
| 230 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 210 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1080 |
| Melting Onset (Solidus), °C | 1030 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 390 |
| Thermal Expansion, µm/m-K | 15 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.5 to 64 | |
| 25 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 230 | |
| 230 to 280 |
| Stiffness to Weight: Axial, points | 3.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 18 |
| Strength to Weight: Axial, points | 4.4 to 7.8 | |
| 9.2 to 10 |
| Strength to Weight: Bending, points | 5.5 to 8.0 | |
| 11 to 12 |
| Thermal Shock Resistance, points | 13 to 24 | |
| 11 to 12 |
Alloy Composition
| Copper (Cu), % | 0 | |
| 99.15 to 99.69 |
| Gold (Au), % | 68 to 70 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0 | |
| 0.010 to 0.030 |
| Platinum (Pt), % | 5.0 to 7.0 | |
| 0 |
| Silver (Ag), % | 23.5 to 26.5 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0.3 to 0.7 |
| Residuals, % | 0 to 0.35 | |
| 0 |