ASTM B522 Class I vs. ZA-27
ASTM B522 class I belongs to the otherwise unclassified metals classification, while ZA-27 belongs to the zinc alloys. There are 23 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B522 class I and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 96 | |
| 78 |
| Elongation at Break, % | 1.1 to 29 | |
| 2.0 to 4.5 |
| Knoop Hardness | 88 to 150 | |
| 120 to 140 |
| Poisson's Ratio | 0.41 | |
| 0.27 |
| Shear Modulus, GPa | 34 | |
| 31 |
| Shear Strength, MPa | 180 to 280 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 490 | |
| 400 to 430 |
| Tensile Strength: Yield (Proof), MPa | 120 to 210 | |
| 260 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 130 |
| Melting Completion (Liquidus), °C | 1030 | |
| 480 |
| Melting Onset (Solidus), °C | 1030 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 530 |
| Thermal Expansion, µm/m-K | 15 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.8 | |
| 53 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 5.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.5 to 64 | |
| 8.1 to 18 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 230 | |
| 420 to 890 |
| Stiffness to Weight: Axial, points | 3.1 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 28 |
| Strength to Weight: Axial, points | 4.4 to 7.8 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 5.5 to 8.0 | |
| 24 to 25 |
| Thermal Shock Resistance, points | 13 to 24 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 25 to 28 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Copper (Cu), % | 0 | |
| 2.0 to 2.5 |
| Gold (Au), % | 68 to 70 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.010 to 0.020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.020 |
| Platinum (Pt), % | 5.0 to 7.0 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.080 |
| Silver (Ag), % | 23.5 to 26.5 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 69.3 to 73 |
| Residuals, % | 0 to 0.35 | |
| 0 |