ASTM B522 Class II vs. ASTM B817 Type II
ASTM B522 class II belongs to the otherwise unclassified metals classification, while ASTM B817 type II belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B522 class II and the bottom bar is ASTM B817 type II.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 96 | |
| 100 |
| Elongation at Break, % | 1.1 to 28 | |
| 3.0 to 13 |
| Poisson's Ratio | 0.41 | |
| 0.32 |
| Shear Modulus, GPa | 34 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 490 | |
| 900 to 960 |
| Tensile Strength: Yield (Proof), MPa | 120 to 210 | |
| 780 to 900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 400 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1580 |
| Melting Onset (Solidus), °C | 1030 | |
| 1530 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 550 |
| Thermal Expansion, µm/m-K | 15 | |
| 9.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 4.6 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.4 to 63 | |
| 26 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 to 230 | |
| 2890 to 3890 |
| Stiffness to Weight: Axial, points | 3.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 34 |
| Strength to Weight: Axial, points | 4.4 to 7.8 | |
| 55 to 58 |
| Strength to Weight: Bending, points | 5.5 to 8.0 | |
| 45 to 47 |
| Thermal Shock Resistance, points | 13 to 24 | |
| 62 to 66 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.0 to 6.0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chlorine (Cl), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 0 | |
| 0.35 to 1.0 |
| Gold (Au), % | 68.5 to 69.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 | |
| 0.35 to 1.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.3 |
| Platinum (Pt), % | 5.5 to 6.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 24.5 to 25.5 | |
| 0 |
| Sodium (Na), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 82.1 to 87.8 |
| Vanadium (V), % | 0 | |
| 5.0 to 6.0 |
| Residuals, % | 0 | |
| 0 to 0.4 |