ASTM B540 Palladium vs. C33200 Brass
ASTM B540 palladium belongs to the otherwise unclassified metals classification, while C33200 brass belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM B540 palladium and the bottom bar is C33200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 1.1 to 14 | |
| 7.0 to 60 |
| Poisson's Ratio | 0.38 | |
| 0.31 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Shear Strength, MPa | 500 to 700 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 830 to 1240 | |
| 320 to 520 |
| Tensile Strength: Yield (Proof), MPa | 620 to 1000 | |
| 110 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 170 |
| Melting Completion (Liquidus), °C | 1220 | |
| 930 |
| Melting Onset (Solidus), °C | 1020 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 380 |
| Thermal Expansion, µm/m-K | 14 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.9 to 5.5 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 to 3.9 | |
| 28 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 100 | |
| 35 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1790 to 4660 | |
| 60 to 960 |
| Stiffness to Weight: Axial, points | 4.7 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 12 | |
| 19 |
| Strength to Weight: Axial, points | 18 to 27 | |
| 11 to 17 |
| Strength to Weight: Bending, points | 15 to 20 | |
| 13 to 17 |
| Thermal Shock Resistance, points | 41 to 61 | |
| 11 to 17 |
Alloy Composition
| Copper (Cu), % | 13.5 to 14.5 | |
| 65 to 68 |
| Gold (Au), % | 9.5 to 10.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Palladium (Pd), % | 34 to 36 | |
| 0 |
| Platinum (Pt), % | 9.5 to 10.5 | |
| 0 |
| Silver (Ag), % | 29 to 31 | |
| 0 |
| Zinc (Zn), % | 0.8 to 1.2 | |
| 29 to 33.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |