ASTM B541 Gold vs. AWS BVAg-6b
Both ASTM B541 gold and AWS BVAg-6b are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM B541 gold and the bottom bar is AWS BVAg-6b.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 93 |
| Poisson's Ratio | 0.4 | |
| 0.35 |
| Shear Modulus, GPa | 38 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1180 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 90 | |
| 160 |
| Melting Completion (Liquidus), °C | 1110 | |
| 870 |
| Melting Onset (Solidus), °C | 930 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 310 |
| Thermal Expansion, µm/m-K | 13 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 9.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.4 | |
| 5.3 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 16 |
| Strength to Weight: Axial, points | 11 to 19 | |
| 5.1 |
| Strength to Weight: Bending, points | 9.8 to 14 | |
| 7.3 |
| Thermal Shock Resistance, points | 36 to 63 | |
| 7.4 |
Alloy Composition
| Cadmium (Cd), % | 0 | |
| 0 to 0.0010 |
| Carbon (C), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 13.5 to 15.5 | |
| 49 to 51 |
| Gold (Au), % | 70.5 to 72.5 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.0020 |
| Platinum (Pt), % | 8.0 to 9.0 | |
| 0 |
| Silver (Ag), % | 4.0 to 5.0 | |
| 49 to 51 |
| Zinc (Zn), % | 0.7 to 1.3 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.4 | |
| 0 |