ASTM B541 Gold vs. C35600 Brass
ASTM B541 gold belongs to the otherwise unclassified metals classification, while C35600 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B541 gold and the bottom bar is C35600 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Poisson's Ratio | 0.4 | |
| 0.31 |
| Shear Modulus, GPa | 38 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1180 | |
| 340 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 90 | |
| 170 |
| Melting Completion (Liquidus), °C | 1110 | |
| 900 |
| Melting Onset (Solidus), °C | 930 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 to 12 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.0 to 6.2 | |
| 29 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.4 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 19 | |
| 11 to 22 |
| Strength to Weight: Bending, points | 9.8 to 14 | |
| 13 to 21 |
| Thermal Shock Resistance, points | 36 to 63 | |
| 11 to 22 |
Alloy Composition
| Copper (Cu), % | 13.5 to 15.5 | |
| 60 to 63 |
| Gold (Au), % | 70.5 to 72.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 2.0 to 3.0 |
| Platinum (Pt), % | 8.0 to 9.0 | |
| 0 |
| Silver (Ag), % | 4.0 to 5.0 | |
| 0 |
| Zinc (Zn), % | 0.7 to 1.3 | |
| 33.4 to 38 |
| Residuals, % | 0 | |
| 0 to 0.5 |