ASTM B563 Pd-Ag-Cu vs. ACI-ASTM CG6MMN Steel
ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals classification, while ACI-ASTM CG6MMN steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is ASTM B563 Pd-Ag-Cu and the bottom bar is ACI-ASTM CG6MMN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 7.0 to 17 | |
| 34 |
| Poisson's Ratio | 0.37 | |
| 0.28 |
| Shear Modulus, GPa | 37 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 1170 | |
| 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 300 |
| Melting Completion (Liquidus), °C | 1180 | |
| 1420 |
| Melting Onset (Solidus), °C | 1030 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 480 |
| Thermal Expansion, µm/m-K | 14 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 7.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 24 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 22 |
| Thermal Shock Resistance, points | 39 to 61 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 20.5 to 23.5 |
| Copper (Cu), % | 15.5 to 16.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 51.9 to 62.1 |
| Manganese (Mn), % | 0 | |
| 4.0 to 6.0 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 3.0 |
| Nickel (Ni), % | 0.8 to 1.2 | |
| 11.5 to 13.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.4 |
| Palladium (Pd), % | 43 to 45 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Platinum (Pt), % | 0.8 to 1.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 37 to 39 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.3 |
| Residuals, % | 0 to 0.4 | |
| 0 |