ASTM B563 Pd-Ag-Cu vs. CC765S Brass
ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals classification, while CC765S brass belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is ASTM B563 Pd-Ag-Cu and the bottom bar is CC765S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 7.0 to 17 | |
| 21 |
| Poisson's Ratio | 0.37 | |
| 0.31 |
| Shear Modulus, GPa | 37 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 1170 | |
| 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 180 |
| Melting Completion (Liquidus), °C | 1180 | |
| 860 |
| Melting Onset (Solidus), °C | 1030 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 400 |
| Thermal Expansion, µm/m-K | 14 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.6 to 6.7 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.6 to 5.5 | |
| 34 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 14 | |
| 20 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 19 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 18 |
| Thermal Shock Resistance, points | 39 to 61 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.5 to 2.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 15.5 to 16.5 | |
| 51 to 65 |
| Iron (Fe), % | 0 | |
| 0.5 to 2.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.5 |
| Manganese (Mn), % | 0 | |
| 0.3 to 3.0 |
| Nickel (Ni), % | 0.8 to 1.2 | |
| 0 to 6.0 |
| Palladium (Pd), % | 43 to 45 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Platinum (Pt), % | 0.8 to 1.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 37 to 39 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 1.0 |
| Zinc (Zn), % | 0 | |
| 19.8 to 47.7 |
| Residuals, % | 0 to 0.4 | |
| 0 |