ASTM B563 Pd-Ag-Cu vs. C49300 Brass
ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals classification, while C49300 brass belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM B563 Pd-Ag-Cu and the bottom bar is C49300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 7.0 to 17 | |
| 4.5 to 20 |
| Poisson's Ratio | 0.37 | |
| 0.31 |
| Shear Modulus, GPa | 37 | |
| 40 |
| Shear Strength, MPa | 470 to 690 | |
| 270 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 1170 | |
| 430 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 170 |
| Melting Completion (Liquidus), °C | 1180 | |
| 880 |
| Melting Onset (Solidus), °C | 1030 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 380 |
| Thermal Expansion, µm/m-K | 14 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.6 to 6.7 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.6 to 5.5 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 14 | |
| 19 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 39 to 61 | |
| 14 to 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Bismuth (Bi), % | 0 | |
| 0.5 to 2.0 |
| Copper (Cu), % | 15.5 to 16.5 | |
| 58 to 62 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 0.8 to 1.2 | |
| 0 to 1.5 |
| Palladium (Pd), % | 43 to 45 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Platinum (Pt), % | 0.8 to 1.2 | |
| 0 |
| Selenium (Se), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 37 to 39 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.0 to 1.8 |
| Zinc (Zn), % | 0 | |
| 30.6 to 40.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |