ASTM B596 Au-Cu vs. Solder Alloy 162
Both ASTM B596 Au-Cu and solder alloy 162 are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ASTM B596 Au-Cu and the bottom bar is solder alloy 162.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 35 |
| Elongation at Break, % | 4.3 to 17 | |
| 36 |
| Poisson's Ratio | 0.41 | |
| 0.4 |
| Shear Modulus, GPa | 36 | |
| 12 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 620 | |
| 41 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 44 |
| Melting Completion (Liquidus), °C | 1060 | |
| 220 |
| Melting Onset (Solidus), °C | 930 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 180 |
| Thermal Expansion, µm/m-K | 14 | |
| 25 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.7 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 18 | |
| 9.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 2.1 |
| Stiffness to Weight: Bending, points | 8.5 | |
| 12 |
| Strength to Weight: Axial, points | 6.8 to 9.4 | |
| 1.2 |
| Strength to Weight: Bending, points | 7.1 to 8.8 | |
| 2.8 |
| Thermal Shock Resistance, points | 22 to 30 | |
| 3.3 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 9.0 to 11 | |
| 1.2 to 1.6 |
| Gold (Au), % | 89 to 91 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 47.3 to 49.3 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 49.5 to 50.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.4 | |
| 0 |