ASTM B596 Au-Cu vs. R05252 Alloy
Both ASTM B596 Au-Cu and R05252 alloy are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM B596 Au-Cu and the bottom bar is R05252 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 4.3 to 17 | |
| 23 |
| Poisson's Ratio | 0.41 | |
| 0.33 |
| Shear Modulus, GPa | 36 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 620 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 140 |
| Thermal Expansion, µm/m-K | 14 | |
| 6.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 18 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 6.5 |
| Stiffness to Weight: Bending, points | 8.5 | |
| 12 |
| Strength to Weight: Axial, points | 6.8 to 9.4 | |
| 5.2 |
| Strength to Weight: Bending, points | 7.1 to 8.8 | |
| 6.1 |
| Thermal Shock Resistance, points | 22 to 30 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 9.0 to 11 | |
| 0 |
| Gold (Au), % | 89 to 91 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 0 | |
| 0 to 0.010 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Tantalum (Ta), % | 0 | |
| 88.8 to 91 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 9.0 to 11 |
| Residuals, % | 0 to 0.4 | |
| 0 |