ASTM B617 Coin Silver vs. EN-MC21110 Magnesium
ASTM B617 coin silver belongs to the otherwise unclassified metals classification, while EN-MC21110 magnesium belongs to the magnesium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is EN-MC21110 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 75 | |
| 46 |
| Elongation at Break, % | 1.1 to 22 | |
| 2.8 to 6.7 |
| Poisson's Ratio | 0.37 | |
| 0.29 |
| Shear Modulus, GPa | 28 | |
| 18 |
| Shear Strength, MPa | 180 to 290 | |
| 120 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 520 | |
| 200 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 350 |
| Melting Completion (Liquidus), °C | 870 | |
| 600 |
| Melting Onset (Solidus), °C | 780 | |
| 500 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 990 |
| Thermal Expansion, µm/m-K | 19 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 83 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 72 | |
| 61 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 1.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 | |
| 15 |
| Stiffness to Weight: Bending, points | 14 | |
| 69 |
| Strength to Weight: Axial, points | 7.7 to 14 | |
| 33 to 44 |
| Strength to Weight: Bending, points | 9.3 to 14 | |
| 45 to 54 |
| Thermal Shock Resistance, points | 14 to 25 | |
| 12 to 16 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 7.0 to 8.7 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 9.0 to 10.4 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.0050 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 89.6 to 92.6 |
| Manganese (Mn), % | 0 | |
| 0.1 to 0.35 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Silver (Ag), % | 89.6 to 91 | |
| 0 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0.35 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.010 |